Polyvinyl Alcohol Fiber PVA Fiber Substitution of Asbestos
Basic Info

Model No.:  Elite-PVA

Product Description Model NO.: Elite-PVA Material: PVA Fiber Type: PVA, Microfiber Color: Light Yellow Function: High Strength Fiber Product Name: Polyvinyl Alcohol /PVA Fiber Raw Material: Polyvinyl Alcohol Tenacity: 11.5cn/Dtex Min. Density: 1.29g/cm3 Hot Water Solubility (90c,1hour): ≤2% Trademark: elite-indus Origin: Hefei Usage: Concrete Feature: Reinforcement Pattern: Jacquard Width: 47/48" Structure: Synthetic Carbon Chain Length: 6mm/12mm Fiber Diameter: 2.0+/-0.25dtex Modulus: 290+/-20cn/Dtex Elongation: 7.5% Max. Certificate: ISO Specification: CE HS Code: 5503900000                      Polyvinyl Alcohol Fiber PVA Fiber Substitution of Asbestos
 PVA Fiber introduction:    Polyvinyl alcohol fiber with high strength and high modulus polyvinyl alcohol (PVA) as the main raw material, made by wet spinning process.  The product has a high modulus, high strength, low elongation, pollution-free, non-toxic, and with acid, alkali, salt, abrasion, sunlight, corrosion, enzymes borers, cracking, anti-penetration, anti-UV, antiaging properties. The essential characteristic of these reinforcements is to absorb and distribute throughout the entire length - and thus attenuate - the tensions that are created in the material by an external load applied to the object

Polyvinyl Alcohol Fiber PVA Fiber Substitution of Asbestos

  PVA Fiber Performance:   1. With the purpose of high modulus, high strength, alkali and acid resistance, heat resistance. It also has good compatibility with cement and other macromolecule material. 2. mainly be used in construction, cement industry, non asbestos material for heat and attrition resistance,plastic and rubber reinforcement. 3. It is the good substitution of Abestos.     PVA Fiber Production Line:

Polyvinyl Alcohol Fiber PVA Fiber Substitution of Asbestos

PVA Fiber application:   (1) high strength and high modulus polyvinyl alcohol fiber is an excellent substitute for asbestos Fibers and glass fibers. (2) polyvinyl alcohol fiber cement products are widely used in construction, such as fiber cement boards, tiles, pipes and so on.  (3) high strength and high modulus PVA fiber tow in water conservancy construction, instead of steel as reinforcement belt (4) high strength and high modulus PVA fiber can also be used for advanced road construction, airport runways, tunnels, bridges and other construction. (5) the production of high strength rope, safety net. (6) rubber tires with reinforced material for conveyor belts, fire hoses, hoses and other preparation. (7) plastic reinforcements.

Polyvinyl Alcohol Fiber PVA Fiber Substitution of Asbestos
PVA Fiber advantage:
  PVA fiber has high strength and modulus of elasticity compare with other general organic fiber used for cement reinforcing widely. As below:
 

 

Tensile

strength

(MPa)

Young's

modulus

(GPa)

Fiber

elongation

(%)

Density

Remarks

PVA fiber

880~1600

25~40

6~10

1.30

-

PP fiber

600

5

25

0.91

Floats in water

Nylon fiber

750~900

3.4~4.9

13~25

1.10

-

Polyethylene fiber

250~700

1.4~2.2

10~15

0.95

-

High performance

polyethylene fiber

2700

120

5

0.97

Expensive

Steel fiber

1200

200

3~4

7.85

Heavy, rusts

AR glass fiber

2200

80

0~4

2.78

Weak in alkali

Asbestos

620

160

-

2.55

Health risky  


Note:Like steel and glass fiber, PVA fibers have a modulus of elasticity, namely resistance to stretching, greater than normal concrete. Fine polypropylene, nylon and the other synthetic fibers used in concrete serve to restrain plastic shrinkage during the first 24 hours after concrete is poured. It is said that PVA fiber has higher tenacity and modulus, makes better performance for cracking control for long terms. Also regarding to structural applications with coarse fiber, high tensile strength and modulus may work effectively.
PVA fiber Specification:  

Material:

Polyvinyl Alcohol

Diameter:

 2.0+/-0.25dtex

Tenacity: 

11.5CN/dtex min.

Elongation:

  7.5% max.

Modulus (0.1-0.4%):

290+/-20CN/dtex

Density: 

  1.29g/cm3

Hot Water Solubility (90ºC,1hour)

 ≤2%

Length:

 6mm multiple

Formula  

   (CH2CHOH)n

  PVA fiber Packing:     200kgs net per plastic woven bag,1.6MT/ Pallet,12.8TM/20'gp, 25.60MT/1X40`HQ

Contact us if you need more details on PVA Fiber. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Polyvinyl Alcohol Fiber、PVA Staple Fiber. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Concrete Additives > PVA Fiber